Alloy H Steels - Heat Chemical Ranges and Limits Alloy H Steel Compositions
Chemical Composition, percent AISI or SAE Steel No. 1330H 1335H 1340H 1345H 4027H 4028H* 4032H 4037H 4042H 4047H 4118H 4130H 4135H 4137H 4140H 4142H 4145H 4147H 4150H 4161H 4320H 4340H E4340H** 4419H 4620H 4621H 4626H 4718H 4720H 4815H 4817H 4820H 50B40H 50B44H 5046H 50B46H 50B50H 50B60H 5120H C Mn SI NI Cr Mo .27-.33 1.45-2.05 .15- 35 .32-.38 1.45-2.05 .15-.35 .37-.44 1.45-2.05 .15-.35 .42-.49 1.45-2.05 .15-.35 .24-.30 .60-1.00 .15-.35 .24-.30 .60-1.00 .15-.35 .29-.35 .60-1.00 .15-.35 .39-.41 .60-1.00 .15-.35 .39-.46 .60-1.00 .15-.35 .44-.51 .60-1.00 .15-.35 .17-.23 .60-1.00 .15-.35 .27-.33 .30-.70 .15-.35 .20-.30 .20-.30 .20-.30 .20-.30 .30-.70 .75-1.20 .20-.30 .20-.30 .08-.15 .15-.25 .15-.25 .15-.25 .15-.25 .15-.25 .15-.25 .15-.25 .15-.25 .25-.35 .20-.30 .20-.30 .20-.30 .45-.60 .32-.38 .60-1.00 .15-.35 .34-.41 .60-1.00 .15-.35 .37-.44 .65-1.10 .15-.35 .39-.46 .65-1.10 .15-.35 .42-.49 .65-1.10 .15-.35 .44-.51 .65-1.10 .15-.35 .47-.54 .65-1.10 .15-.35 .55-.65 .65-1.10 .15-.35 .17-.23 .37-.44 .37-.44 .17-.23 .17-.23 .40-.70 .55-.90 .60-.95 .35-.75 .35-.75 .75-1.20 .75-1.20 .75-1.20 .75-1.20 .75-1.20 .75-1.20 .75-1.20 .65-.95 .15-.35 1.55-2.00 .35-.65 .15-.35 1.55-2.00 .65-.95 .15-.35 1.55-2.00 .65-.95 .15-.35 .15-.35 1.55-2.00 .30-.60 .20-.30 .20-.30 .15-.25 .30-.40 .15-.25 .20-.30 .20-.30 .20-.30 .17-.23 .60-1.00 .15-.35 1.55-2.00 .23-.29 .15-.21 .17-.23 .12-.18 .14-.20 .17-.23 .40-.70 .60-.95 .45-.75 .30-.70 .30-.70 .40-.80 .15-.35 .65-1.05 .15-.35 .85-1.25 .15-.35 .85-1.25 .30-. 60 .15-.35 3.20-3.80 .15-.35 3.20-3.80 .15-.35 3.20-3.80 .30-.70 .30-.70 .13-.43 .13-.43 .30-.70 .30-.70 .60-1.00 .37-.44 .65-1.10 .15-.35 .42-.49 .65-1.10 .15-.35 .43-.50 .65-1.10 .15-.35 .43-.50 .65-1.10 .15-.35 .47-.54 .65-1.10 .15-.35 .55-.65 .65-1.10 .15-.35 .17-.23 .60-1.00 .15-.35 5130H 5132H 5135H 5140H 5145H 5147H 5150H 5155H 5160H 51B60H 6118H 6150H 81B45H .27-.33 .60-1.10 .15-.35 .29-.35 .32-.38 .50-.90 .50-.90 .15-.35 .15-.35 .75-1.20 .65-1.10 .70-1.15 .60-1.00 .60-1.00 .80-1.25 .60-1.00 .60-1.00 .60-1.00 .15-.45
.60-1.00 .40-.80 .75-1.20 .30-.60 .10-.15 V .15 Min. V .08-.15 .37-.44 .60-1.00 .15-.35 .42-.49 .60-1.00 .15-.35 .45-.52 .60-1.05 .15-.35 .47-.54 .60-1.00 .15-.35 .50-.60 .60-1.00 .15-.35 .55-.65 .65-1.10 .15-.35 .55-.65 .65-1.10 .15-.35 .15-.21 .40-.80 .15-.35 .47-.54 .60-1.00 .15-.35 .42-.49 .70-1.05 .15-.35 * Sulfur = .035- 0.50% ** Sulfur = .025 max.
Chemical Composition, percent AISI or SAE Steel No. 8617H 8620H 8622H 8625H 8627H 8630H 86B30H 8637H 8640H 8642H 8645H 86B45H 8650H 8655H 8660H 8720H 8740H 8822H 9260H 9310H 94B15H 94B17H 94830H C Mn Sl .15- .35 .15- .35 .15- .35 .15- .35 .15- .35 .15- .35 .15- .35 .15- .35 .15- .35 .15- .35 .15- .35 .15- .35 .15- .35 .15- .35 .15- .35 .15- .35 .15- .35 .15- .35 Ni .35- .75 .35- .75 .35- .75 .35- .75 .35- .75 .35- .75 .35- .75 .35- .75 .35- .75 .35- .75 .35- .75 .35- .75 .35- .75 .35- .75 .35- .75 .35- .75 .35- .75 .35- .75 Cr .35- .65 .35- .65 .35- .65 .35- .65 .35- .65 .35- .65 .35- .65 .35- .65 .35- .65 .35- .65 .35- .65 .35- .65 .35- .65 .35- .65 .35- .65 .35- .65 .35- .65 .35- .65 Mo .15- .25 .15- .25 .15- .25 .15- .25 .15- .25 .15- .25 .15- .25 .15- .25 .15- .25 .15- .25 .15- .25 .15- .25 .15- .25 .15- .25 .15- .25 .20- .30 .20- .30 .30- .40 .14- .20 .60- .95 .17- .23 .60- .95 .19- .25 .60- .95 .22- .28 .60- .95 .24- .30 .60- .95 .27- .33 .60- .95 .27- .33 .60- .95 .34- .41 .70- 1.05 .37- .44 .70- 1.05 .39- .46 .70- 1.05 .42- .49 .70- 1.05 .42- .49 .70- 1.05 .47- .54 .70- 1.05 .50- .60 .70- 1.05 .55- .65 .70- 1.05 .17- .23 .60- .95 .37- .44 .70- 1.05 .19- .25 .70- 1.05 .55- .65 .65- 1.10 1.70-2.20 .07- .13 .40- .70 .12- .18 .70- 1.05 .14- .20 .70- 1.05 .27- .33 .70- 1.05 .15- .35 .15- .35 .15- .35 .15- .35
2.95.3.55 1.00-1.45 .08- .15 .25- .65 .25- .65 .25- .65 .25- .55 .25- .55 .25- .55 .08- .15 .08- .15 .08- .15 NOTE 1. The Phosphorus .035 max. and the sulfur = .040 max. unless indicated otherwise.
Maximum per cent P Basic electric Basic open hearth or basic oxygen or TOC Acid electric Acid open hearth
NOTE 2. Minimum silicon limit for acid open hearth or acid electric furnace alloy steel is 15 per cent.
NOTE 3. Small quantities of certain elements are present in alloy steels which are not specified or required. These elements are considered as incidental and may be present to the following maximum amounts: Copper, .35 per cent; Nickel, .25 per cent; Chromium, .20 per cent; and Molybdenum, .06 per cent.
NOTE 4. The chemical ranges and limits shown this Table and In the notes below this Table are subject to
the product analysis tolerances shown In the AISI Manual. (Dated March, 1986).
NOTE 5. Standard H-Steels can be produced with a lead range of .15/.35 per cent. Such steels are identified by inserting the fetter \"L\" between the second and third numerals of the AISI number, e.g., 41 L
40 H. Lead is reported only as a range of .15/.35 per cent.
NOTE 6. Where minimum and maximum sulfur content is shown It is indicative of resulfurized steel.
.025 .035 .050 .050 S .025 .040 .050 .050
美国钢号表示法
美国对结构钢、工具钢和不锈耐热钢的命名编号方法各不相同。现将各类钢号的表示方法分述如下。 Ⅰ.结构网
一般采用美国钢铁学会（American Iron and Steel Instute）的AISI标准和美国汽车工程师学会（American Society of Automotive Engineer）的SAE标准，也有采用所谓“政府标准”，即FS（Federal Specification）标准体系的。实际上这三种标准体系的表示方法基本相同，只是前置符号有些不同。 ） SAE标准的钢号表示法
钢号一般由四位数字组成，前两位表示钢类，后两位表示钢的平均含碳量的万分之几的数值。具体编号系统为：
1×××——碳素钢，其中包括：
10××——一般碳素钢，如1035为平均含碳0.35%的碳素钢。
11××——易切削碳素钢，如1132为平均含031%C、1.5%Mn、0.04%P、0.1%S的易削钢。 13××——锰结构钢，如1335为平均含0.35%C、0.3%Si、1.8%Mn的锰钢。
2×××——镍钢，第二位数字表示平均含镍量的百分数近似值，如2517平均含5%Ni、0.17%C的镍钢。 3×××——镍铬钢，第二位数字也表示含镍量，如3310为平均含3%Ni、1.5%Cr、0.1%C的镍铬钢。 4×××——含钼钢，第二位数字表示是否尚有其他合金元素的含量等。其中包括：4×××、44××、45××表示含钼量不同的钼钢；
43××、47××表示不同的镍铬钼含量的钢； 46××、48××表示不同镍钼含量的钢。
5×××——铬钢，第二位数字表示含铬量，如5046为含0.3%Cr、0.46%C的低铬钢；5147为含1.0%Cr、0.47%C的低铬钢。
滚动轴承钢的钢号由五位数字组成，第二位数字表示含铬量，最后三位数字表示含碳量，例如： 50100为含1.0%C、0.5%Cr的轴承钢，相当我国的GCr6； 51100为含1.0%C、1.0%Cr的轴承钢，相当我国的GCr9； 52100为含1.0%C、1.5%Cr的轴承钢，相当我国的GCr15。
61××——平均含0.95%Cr、含V>0.10%的铬钒钢，如6150为含0.5%C、1%Cr、0.15%V的铬钒钢。 72××——钨钢，如7260为含0.8%Cr、1.8%W、0.6%C的铬钨钢。
8×××——低镍铬钼钢，第二位数字表示某一镍、铬含量和不同含钼量的钢。其中86××表示平均含0.55%Ni、0.50%Cr、0.20%Mo的钢；87××表示含0.55%Ni、0.50%Cr、0.25%Mo的钢；88××表示含有0.55%Ni、0.50%Cr、0.35%Mo的钢。
9×××——主要由第二位数字决定属于哪个钢类。其中92××为含硅为约2%的硅锰合钢；93××、94××、97××、98××等为不同镍、铬钼含量的钢。
另外，有些钢号中间插入字母或在末尾标有字母。例如： 50B44为含硼<0.0005%的铬硼钢（“B”为Boron的缩写）； 12L14为含铅0.15～0.35%的易削钢（“L”为Lead的缩写）；
4140H为有一定淬透性要求的铬钼钢（“H”为Hardenability的缩写）。
） AISI标准的钢号表示法
与SAE标准相同，不过有些钢号带有前置或后置字母。如对碳素钢和易削钢的钢号前冠以“C”表示平炉钢，冠以“B”表示酸性转炉钢，例如C1020、C1108、B1010、B1112等；对合金钢的钢号冠以“E”表示电炉钢，冠以“TS”表示试验性的标准钢号，例如E3310、TS4130；在钢号末尾标以“F”也表示易削钢。 ） FS标准表示法
与SAE标准亦相同，只是在钢号前冠以“FS”如FS1335；对电炉钢和酸性转炉钢分别表示为FSE××××和FSB××××。
Ⅱ.工具钢
采用AISI—SAE的统一编号系统，钢号由表示钢类的字母和顺序号组成，这种编号方法不能表示出化学成分。具体编号系统如下：
W×——水淬工具钢，一般系碳钢或含少量铬、钒的钢。如W5为含1.1%C、0.5%Cr的钢。 O×——油淬冷作工具钢，包括含碳0.9～1.45%的CrWMn钢、Mn钢、SiMo钢、CrWMo钢。 S×——耐冲击工具钢，包括含碳0.5%CrW钢、SiMo钢和SiMn钢。
A×——空冷硬化中合金冷作工具钢，包括含碳0.70%的CrMo和CrMnMo钢。
D×——高碳高铬型冷作工具钢，包括含1.0～2.25%C和约12%Cr的Cr钢、CrMo钢、CrWSi钢CrWCo钢。
H×——热作工具钢，包括H1×代表中碳中铬热模钢，H2×代表钨系热作模具钢和H4×代表钼系热作模具钢。
T×——钨系高速工具钢，如T1相当我国的W18Cr4V钢。 M×——钼系高速工具钢，如M2相当我国的W6Mo5Cr4V2钢。
L×——低合金特种用途工具钢，包括含0.5～1.1%的Cr钢、CrV钢、CrMnMo钢、CrNiMo钢和CrMo钢。
F×——碳钨工具钢，包括含1.0～1.25%C、1.25～3.50%W的W钢和CrW钢。
P×——低碳型工具钢，包括含碳<0.7～0.30%的Cr钢、CrNi钢、CrMo钢和CrNiMo钢。 Ⅲ.不锈钢和耐热钢
其中锻造钢的钢号主要采用AISI的编号系统；而铸钢的钢号除了采用上述编号系统外，大多采用美国铸造学会（Alloy Casting Institute）ACI标准的编号系统。分述如下： ） AISI标准的钢号表示法
对于锻造钢和铸钢，钢号均由三位数字组成，第一位数字表示钢类，后两位表示顺序号。具体编号系统为： 2××——铬锰镍氮奥氏体钢，如“202”为含C≤0.15%、Mn≤10.0%、Si≤1.0%、Cr17～19%、Ni4～6%、N≤0.25%的奥氏体不锈耐热钢。
3××——镍铬奥氏体钢，如“302”相当于我国1Cr18Ni9奥氏体不锈钢。
4××——高铬马氏体钢和低碳高铬铁素体不锈耐热钢，如“403”相当于1Cr13；“430”相当于Cr17钢。
5××——低铬马氏体钢，如“501”相当于我国的Cr5Mo耐热钢。
） SAE标准的钢号表示法
钢号由五位数字组成，前三位数字表示钢类，后两位表示顺序号。具体编号系统为：
303××——镍铬奥氏体不锈耐热钢（锻造钢），例如“30316”相当于AISI的“316”钢。
514××——高铬马氏体和低碳高铬铁素体不锈耐热钢（锻造钢），如“51414”相当于AISI的“414”钢。
60×××——用于650ºC以下的耐酸钢（铸铁），×××为与AISI相同的编号数字，例如“60316”
相当于AISI的“316”钢。
70×××——用于超过650ºC的耐热钢（铸钢），例如“70334”钢相当于AISI的“334”钢。 由上可知，SAE编号系统的最后三位数字实际上和AISI的编号系统是一致的。
） ACI标准的钢号表示法
钢号由两个字母组成或在字母后加上表示含碳量的数字及表示合金元素的字母。钢号的第一个字母一般采用“C”和“H”。C型钢表示在650ºC以下使用的耐酸钢；H型钢表示用于超过650ºC的耐热钢。 C型钢钢号的第二个字母A、B、C、D„„表示不同含镍量（从<1.0%递增至～68%，分14级）。在该字母后再标以数字，表示含碳量的万分之几，在数字与字母间加一短线。例如“CE—30”为含C<0.30%，Cr26.0～30.0%、Ni8～11%的耐酸钢。
H型钢钢号的第二个字母亦为A、B、C、D„„，表示不同的含镍量。一般不标含碳量的数值。例如“HC”为含C<0.50%、Cr26.0～30.0%、Ni<4%的耐热钢。
在有些钢号的数字后（主要是C型钢）还标有字母，如“C”表示加入Nb，“M”表示加入Mo，“F”表示具有易削性。例如“CF—8C”、“CF—16F”。
此外，还有美国材料实验协会（American Society of Testing Materials）的ASTM标准。钢号开头一般冠以字母“A”表示铁基材料，接着是序号数字，最后标年号数，也有在年号后标“T”表示试验性的钢号。例如“ASTMA366—62T”为62年制定的含0.15%C、00.5%Mn、0.04%S和P的供冷轧薄板用的试验性钢种。